Sikafloor® MultiDur WS-18
Sikafloor® MultiDur WS-18 is a water-based, low-VOC epoxy floor coating system that provides a smooth finish.
- Suitable for floors with normal to medium-heavy mechanical and chemical loading
- Low VOC emissions
- Seamless
- Good resistance to chemicals
- Good mechanical resistance
- Easy application
- Good water vapour permeability
- Dilutable by water
- Low odour
- Easy to clean
Utilizare
Sikafloor® MultiDur WS-18 is used for:- Storage areas
- Assembly halls
- Manufacturing facilities and workshops
- Logistics facilities and warehouses
- The System may only be used for interior applications.
- The System may only be used by experienced professionals.
Avantaje
- Suitable for floors with normal to medium-heavy mechanical and chemical loading
- Low VOC emissions
- Seamless
- Good resistance to chemicals
- Good mechanical resistance
- Easy application
- Good water vapour permeability
- Dilutable by water
- Low odour
- Easy to clean
Culoare
Cured system colour | Available in various colour shades |
Aspect
Smooth, semi-gloss finish
Detalii Sistem
APROBĂRI / CERTIFICĂRI
-
Reaction to fire EN 13501-1:2018, Sikafloor® MultiDur WS-18, GHENT, Test report No. CR 23-0398-01
Structura sistemului
Sikafloor® MultiDur WS-18
| Product | Layer | |
| 1. | Primer | Sikafloor®-2510 W + 10 % water by weight |
| 2. | Top coat | Sikafloor®-2510 W |
Add coloured chips or antislip agent to the top coat to increase slip resistance.
Transparent Sikafloor®-2510 W can be used as a primer and a top coat to enhance the natural aesthetic of concrete or mineral substrates.
Sistemul de bază chimic
Water-based epoxy
Grosime nominală
0.2 mm to 0.3 mm
Rezistență la abraziune
Cured 7 days at +23 °C | 723 mg (H22 wheel / 1000 cycles / 1000 g) |
Aderență prin încercarea la smulgere
≥ 1.5 MPa | (EN 1542) |
Reacție la foc
Class Bfl-s1 | (EN 13501-1) |
Rezistență la alunecare
| With coloured chips | R 9 |
| With antislip agent | R 9 |
Aplicare
Temperatura ambientală a aerului
Maximum | +30 °C |
Minimum | +10 °C |
Umiditatea relativă a aerului
Maximum | 75 % r.h. |
Punct de rouă
Refer to the individual Product Data Sheet.
Temperatura suportului
Maximum | +30 °C |
Minimum | +10 °C |
Conținut de umiditate în suport
≤ 6 % parts by weight using the calcium carbide method (CM-method)
Timp de așteptare / Reacoperire
Before applying Sikafloor®-2510 W on Sikafloor®-2510 W, allow:
Substrate temperature | Minimum | Maximum |
+10 °C | 48 hours | 7 days |
+20 °C | 20 hours | 6 days |
+30 °C | 10 hours | 3 days |
If relative air humidity is ≥ 75 % the waiting time is increased by at least 24 hours.
Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.
Produsul aplicat este utilizabil după
Temperature | Foot traffic | Light traffic | Full cure |
+10 °C | 48 hours | 5 days | 10 days |
+20 °C | 20 hours | 3 days | 7 days |
+30 °C | 10 hours | 2 days | 5 days |
Note: Times apply when the last layer of the system has been applied. Times are affected by changing ambient conditions, particularly temperature and relative humidity.
Consum
Layer | Product | Consumption |
Primer | 1 × Sikafloor®-2510 W + 10 % by weight water | 0.15–0.2 kg/m² |
Top coat | 1–2 × Sikafloor®-2510 W (Optional) Coloured chips or (Optional) Antislip agent | 0.15–0.2 kg/m² per layer 0.05 kg/m² 4 % by weight |
Note: Consumption data is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply the Product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.